| 80-100 | TEST METHOD | MIN | MAX | Penetration at 25 °C, 0.1m | 80 | 100 | ASTM D5 | Softening Point (R&B), °C | 44 | 49 | ASTM D 36 | Flash Point (COC), °C | - | - | ASTM D 92 | Ductility at 25 °C, cm | 100 | - | ASTM D 113 | Solubility in trlchloroethylene % | 89.5 | - | ASTM D 2042 | Retained Penetration after Thin Film Oven Test, % | - | - | ASTM D5&1754 | Ductility at 25 °C after Thin Film Oven Test, cm | 50 | - | ASTM D 113& 17543 | Loss on heating for 5 h at 163 °C a) Loss by mass% b) Drop in Penetration | - - | 0.5 20 | BS 2000 Part 45 | Complies to | DIN 1995 Part 1 Grade B 80 |
|
|